Dugdale-type crack tip plasticity in orthotropic plates studied by caustics (EN)

Theocaris, PS (EN)

N/A (EN)

Dugdale-Barenblatt (D-B)-type plastic zones developed ahead of cracks in orthotropic plates subjected to simple tension were studied by the method of caustics. Using the D-B model the components of the plastic stress field around the crack tip were derived which created new shapes of the caustics because of the influence of plasticity and anisotropy. A relationship between the plastic stress intensity factor, KIP, and typical geometric elements of the caustics may be established by means of convenient graphs. Application of the method to polycarbonate tension specimens with transverse edge cracks, drawn conveniently to present any amount of anisotropy, indicated the potentialities of the method. © 1992. (EN)

journalArticle

Mathematical Techniques--Numerical Methods (EN)
Plasticity (EN)
Orthotropic Plates (EN)
Fracture Mechanics--Stresses (EN)
Crack Tip Plasticity (EN)
Method of Caustics (EN)
Stress Intensity Factors (EN)
Plates (EN)

Εθνικό Μετσόβιο Πολυτεχνείο (EL)
National Technical University of Athens (EN)

Engineering Fracture Mechanics (EN)

1992


PERGAMON-ELSEVIER SCIENCE LTD (EN)



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.