Durability of Reinforced Lightweight Mortars with Corrosion Inhibitors

δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*
κοινοποιήστε το τεκμήριο

Durability of Reinforced Lightweight Mortars with Corrosion Inhibitors (EN)

Kouloumbi, N (EN)
Batis, G (EN)
Katsiamboulas, A (EN)

N/A (EN)

The aim of this experimental work is the examination of the performance of reinforced mortar specimens containing Greek fine-pumice aggregates together with corrosion inhibitors (sodium nitrite or sodium benzoate or iron oxides) added in order to lower the corrosion rate of steel reinforcement in a chloride environment. The durability of the specimen was evaluated by measuring the corrosion potential and the mass loss time dependence of the steel rebar, the carbonation depth, the porosity, and the compressive strength of the specimens. Correlation of the above results revealed that the corrosion inhibitors examined have a protective effect on the steel, while the changes of the mechanical strength of the relative lightweight mortars are not significant compared to the practical needs. The most efficient inhibitor was sodium nitrite in both concentrations examined, that is, 2 and 5%. (EN)


Concrete aggregates (EN)
Reinforced lightweight mortars (EN)
Steel reinforcements (EN)
Mass loss time dependence (EN)
Mortar (EN)
Sodium nitrate (EN)
Compressive strength (EN)
Correlation methods (EN)
Sodium nitrite (EN)
Reinforced concrete (EN)
Corrosion resistance (EN)
Corrosion inhibitors (EN)
Corrosion (EN)
Concrete testing (EN)
Carbonation (EN)
Concrete reinforcements (EN)
Abrasives (EN)
Porosity (EN)
Lightweight aggregates (EN)
Sodium compounds (EN)

Εθνικό Μετσόβιο Πολυτεχνείο (EL)
National Technical University of Athens (EN)

Cement, Concrete and Aggregates (EN)

Αγγλική γλώσσα



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.