Preparation and characterization of manganese oxidic mesoporous particles obtained via the trinuclear [Mn3O(CH3COO)(6)(pyr)(3)]ClO4 complex

 
Το τεκμήριο παρέχεται από τον φορέα :
Πανεπιστήμιο Ιωαννίνων
Αποθετήριο :
Ιδρυματικό Αποθετήριο Ολυμπιάς
δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*
κοινοποιήστε το τεκμήριο



Preparation and characterization of manganese oxidic mesoporous particles obtained via the trinuclear [Mn3O(CH3COO)(6)(pyr)(3)]ClO4 complex (EN)

Zarlaha, A. D. (EN)

Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Χημείας (EL)
Zarlaha, A. D. (EN)

Manganese oxidic mesoporous particles of nominal size in the micrometer region have been prepared by controlled hydrolysis of the trinuclear complex [Mn3O(CH3COO)(6)(pyr)(3)]ClO4(pyr:pyridine). The cation of the complex, which is unstable in water, was hydrolized in various baths containing additives like M(CH3COO)(2) (M=Mn, Ni), M'(NO3)(2-3) (M'= Ni, Mn, La, Co, Fe), LiOH, and CH3COOH. The resulting dried products of hydrolysis possess surface areas as high as 200-400 m(2)g(-1) at T less than or equal to 300 degrees C, 50-200 m(2)g(-1) around 400 degrees C, and 20-100 m(2)g(-1) at T = 500-600 degrees C depending on the additive. The particle thus obtained shows no hysteresis loop in the adsorption-desorption of N-2 at 77 K. The alpha(s) plots indicate that the obtained solids are mesoporous, The calculated pores are in the range of 5-10 nm, corresponding most probably to interparticle void space. Particle size analysis showed that the formed particles are in the micrometer region and SEM photographs reveal micrometer scale particles, too. Plots of lnV(ads) vs ln[ln(P0/P)], where V-ads is the volume of N-2 adsorbed at T = 77 K and relative pressure P/P-0, reveal a surface dimentionality D of the particles equal to 2.56 +/- 0.05. This value approaches the fractal dimentionality of the Koch pyramid 2.58497, and a model is proposed for building up such Koch-like porous particles from Mn4O or MnO4 tetrahedra. (C) 1998 Academic Press. (EN)

manganese oxide (EN)

Πανεπιστήμιο Ιωαννίνων (EL)
University of Ioannina (EN)

J Colloid Interface Sci (EN)

Αγγλική γλώσσα

1998

<Go to ISI>://000074211500010

Academic Press (EN)



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.