Preparation, characterization and surface acid catalytic activity of microporous clays pillared with Al1-xFexOy (x=0.00 to 1.00) oxidic species

 
Το τεκμήριο παρέχεται από τον φορέα :

Αποθετήριο :
Ιδρυματικό Αποθετήριο Ολυμπιάς
δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*
κοινοποιήστε το τεκμήριο




1999 (EL)

Preparation, characterization and surface acid catalytic activity of microporous clays pillared with Al1-xFexOy (x=0.00 to 1.00) oxidic species (EN)

Stathopoulos, V. N. (EN)

Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Χημείας (EL)
Stathopoulos, V. N. (EN)

Montmorillonite was pillared with mixed oxidic species of the form Al1-xFexOy where x = 0.00, 0.05, 0.15, 0.25, 0.50, 0.75 and 100. The pillaring agent was an alkaline solution of the corresponding quantities of metal nitrates so as to obtain a final ratio (Al + Fe)/OH = 1:2. The specific surface area (BET) of the samples dried at 500 degrees C was found to be 230 +/- 10 m(2) g(-1) for x = 0.00 - 0.50 and similar to 139 +/- 8 m(2) g(-1) for x = 0.75-1.00. The XRD results obtained at low angles from samples oriented along the (001) axis showed gallery heights of the heated solids of 16-17 Angstrom for x = 0.00 - 0.50 and 9.9 - 9.8 Angstrom for x = 0.75 - 1.00. The acidity of the samples, checked by TPD of NH3, varied from similar to 12 x 10(17) sites m(-2) (x greater than or equal to 0.25) to similar to 9 x 10(17) sites m(-2) (x less than or equal to 0.75). The acid catalytic activity of the solids was checked using the isopropanol (IPA) decomposition as a probe reaction. The main products observed were propene (selectivity greater than or equal to 80%) and di-iso-propyl ether (DIPE) (selectivity less than or equal to 20%). The apparent activation energies for the TPA conversion were calculated, and the selectivity dependence on temperature was kinetically modelled. From this, a mechanism was derived to account for the reactions of one or two IPA molecules towards propene or DIPE, respectively, and the dependence of the selectivity on the Al/Fe ratio and the acidity of the solids. (C) 1999 Elsevier Science B.V. All rights reserved. (EN)

acid catalysis (EN)


Microporous and Mesoporous Materials (EN)

Αγγλική γλώσσα

1999


Elsevier (EN)