Electrodeposition of Ni particles on laser nanostructured electrodes for enhanced hydrogen evolution reaction
(EN)
In this study, a two-step electrode fabrication process is used to enlarge the electrocatalytic area of the electrodes and improve the hydrogen evolution reaction. Nickel electrodes were laser-nanostructured, and afterward, they were galvanostatically electrodeposited, a novel approach for electrodes used for HER. SEM and EDX analysis were performed. The electrochemical evaluation provided enhanced values of overpotential (η10 = 108 mV), Tafel slope (b = −121 mV dec−1) and double layer capacitance (1945 μF cm−2) compared to the literature. The stability of the electrodes was tested by its overpotential (|η100|=264 mV) in a current density of 100 mA cm−2.
(EL)
*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.
Βοηθείστε μας να κάνουμε καλύτερο το OpenArchives.gr.
Πολυτεχνείο Κρήτης