Efficiency of natural Greek pozzolan in chloride-induced corrosion of steel reinforcement

δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*
κοινοποιήστε το τεκμήριο

Efficiency of natural Greek pozzolan in chloride-induced corrosion of steel reinforcement (EN)

Pantazopoulou, Paraskevi (EN)
Kouloumbi, Niki (EN)
Batis, George (EN)

N/A (EN)

This experimental work estimates the corrosion behavior in a sodium-chloride environment of steel reinforcements in mortar specimens with 0, 15, and 30% Greek natural pozzolan, cured either for 1, 7, or 28 days. The corrosion resistance was evaluated by measuring the corrosion potential development of steel rebars, their gravimetric mass loss, their anodic potentio-dynamic behavior, and the total- and free-chloride content of the mortars. Additionally, their mineralogical composition was determined by X-ray diffraction (XRD) analysis. The increase of curing time, as well as the addition of the Greek natural pozzolan, for both percentages tested, improved the corrosion behavior. The combination of the pozzolan addition with longer curing time reduces the steel rebars mass loss up to a level of about 40% after five months of exposure. (EN)


Curing time (EN)
Steel reinforcement (EN)
Composition (EN)
Addition reactions (EN)
Mortar (EN)
Corrosion potential (EN)
Gravimetric mass loss (EN)
Pozzolan (EN)
Sodium chloride environment (EN)
Chloride induced corrosion (EN)
Steel (EN)
Corrosion resistance (EN)
Natural Greek pozzolan (EN)
X ray diffraction analysis (EN)
Corrosion (EN)
Curing (EN)
Reinforcement (EN)
Anodic potentio dynamic behavior (EN)

Εθνικό Μετσόβιο Πολυτεχνείο (EL)
National Technical University of Athens (EN)

Cement, Concrete and Aggregates (EN)


ASTM, Philadelphia, PA, United States (EN)

*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.