Evaluation of the behaviour of particulate polymeric coatings in a corrosive environment. Influence of the concentration of metal particles

 
δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*
κοινοποιήστε το τεκμήριο



Evaluation of the behaviour of particulate polymeric coatings in a corrosive environment. Influence of the concentration of metal particles (EN)

Kouloumbi, N (EN)
Kyvelidis, S (EN)
Tsangaris, GM (EN)
Skordos, A (EN)

N/A (EN)

In this work pretreated steel specimens were coated by a spinning process with particulate polymeric composites consisting of an epoxy resin (DOW 331) and iron powder. Applied coatings were roughly 70 mu m thick and the contained quantity of iron particles was varied (7.5, 15, 30% wt./wt.). The effect of the presence of iron particles in the coatings as well as the influence of their concentration on the evaluation of the coatings' behaviour in a corrosive environment (3.58 NaCl) was studied. Electrochemical impedance spectroscopy, corrosion potential, corrosion current density (Tafel) and dielectric measurements were performed. Minor differences in the anticorrosive behaviour of the coatings were observed irrespective of the iron content in the coating. Effective resistance inhibition action of the composite coatings was diminished with the increase of exposure time to the corrosive environment being in all cases very close to that of the pure epoxy resin coatings. (EN)

journalArticle

Spectroscopy (EN)
Corrosive environment (EN)
Particulate polymeric coatings (EN)
Corrosion current density (EN)
Effective resistance inhibition (EN)
Iron (EN)
Corrosive effects (EN)
Corrosion resistance (EN)
Particles (particulate matter) (EN)
Corrosion (EN)
Composite coatings (EN)
Electric variables measurement (EN)
Epoxy resins (EN)
Organic coatings (EN)
Dielectric measurements (EN)
Polymers (EN)
Current density (EN)
Metal particles (EN)
Electrochemical impedance spectroscopy (EN)
Spinning process (EN)

Εθνικό Μετσόβιο Πολυτεχνείο (EL)
National Technical University of Athens (EN)

Progress in Organic Coatings (EN)

1996


ELSEVIER SCIENCE SA LAUSANNE (EN)