Development and application of a holistic model for the steady state growth of porous anodic alumina films

Το τεκμήριο παρέχεται από τον φορέα :
Εθνικό Μετσόβιο Πολυτεχνείο   

Αποθετήριο :
Ψηφιακό Αποθετήριο της Κεντρικής Βιβλιοθήκης του ΕΜΠ | Dspace@NTUA   

δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*



Development and application of a holistic model for the steady state growth of porous anodic alumina films (EN)
Patermarakis, G (EN)
Moussoutzanis, K (EN)
journalArticle (EN)
2014-03-01T01:30:09Z
2009 (EN)
A holistic model was developed and applied to anodic alumina films galvanostatically grown in sulphuric acid solution at different anodising conditions thus characterised by different structural characteristics. The O2- and Al3+ species transport numbers near the metalloxide interface were determined that depended on both temperature and current density. The rate of film thickness growth was found to be proportional to the O2- anionic current through the barrier layer near the metalloxide interface. The results introduced a new growth mechanism theory embracing the rarefaction of barrier layer oxide lattice towards the metalloxide interface. The oxide density near the metalloxide is closely independent of anodising conditions and is related to the transformation of Al lattice to a transient oxide lattice about 37% rarer than that of gamma-Al2O3 that is further suitably transformed to denser, amorphous or nanocrystalline material as this oxide is shifted to the oxide vertical bar electrolyte interface and becomes the pore wall material. This gradual lattice density variability can explain many peculiar properties of anodic alumina films. (C) 2008 Elsevier Ltd. All rights reserved. (EN)
Electrochemistry (EN)
Aluminum sheet (EN)
Anodising (EN)
Species transports (EN)
Aluminum (EN)
Barrier layers (EN)
Metals (EN)
Electrolyte interfaces (EN)
Growth mechanisms (EN)
Steady state growth (EN)
Porous anodic alumina films (EN)
Holistic model (EN)
Oxide lattices (EN)
Pore walls (EN)
Structural characteristics (EN)
Film growth (EN)
Sulfuric acid (EN)
Anodic alumina films (EN)
Lattice density and form variability (EN)
Porous anodic alumina (EN)
Oxide interfaces (EN)
Nanocrystalline materials (EN)
Thickness growths (EN)
Sulphuric acids (EN)
Alumina (EN)
Electrochimica Acta (EN)
Αγγλική γλώσσα
PERGAMON-ELSEVIER SCIENCE LTD (EN)
Εθνικό Μετσόβιο Πολυτεχνείο
Ψηφιακό Αποθετήριο της Κεντρικής Βιβλιοθήκης του ΕΜΠ | Dspace@NTUA
Κεντρική Βιβλιοθήκη Ε.Μ.Π.
Ιδρυματικό Αποθετήριο
Δημοσιεύσεις μελών Δ.Ε.Π. σε περιοδικά



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.