EFFECT OF M7C3-]M23C6 TRANSFORMATION ON FRACTURE-BEHAVIOR OF CAST FERRITIC STAINLESS-STEELS

Το τεκμήριο παρέχεται από τον φορέα :
National Technical University of Athens   

Αποθετήριο :
Digital Library of National Technical University of Athens | Dspace@NTUA   

δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*



EFFECT OF M7C3-]M23C6 TRANSFORMATION ON FRACTURE-BEHAVIOR OF CAST FERRITIC STAINLESS-STEELS (EN)
VARDAVOULIAS, M (EN)
PAPADIMITRIOU, G (EN)
PANTELIS, D (EN)
journalArticle (EN)
2014-03-01T01:42:05Z
1993 (EN)
The fracture behaviour of three 29 wt-%Cr ferritic steels, two containing zirconium and titanium respectively, has been investigated in the as cast condition and after annealing at 660-degrees-C for different times up to 2210 h. The fracture energy and the mode of fracture depend on both the morphology and the nature of the eutectic, which consists of carbides and ferrite. In the as cast condition, fracture is predominantly transgranular cleavage and it can be associated with the discontinuous morphology of the M7C3 carbides present in the eutectic as coarse particles surrounded by the eutectic ferrite. After prolonged heating, the ambient fracture energy decreases and the interdendritic mode of fracture is enhanced. This change in fracture mechanism is associated with transformation of the M7C3 to M23C6 carbides. The M23C6 carbides, unlike the coarse M7C3 carbides, form a continuous network within the eutectic mixture and constitute an easy path for crack propagation. The zirconium and titanium additions result in a more massive morphology of the carbides in the eutectic mixture and accelerate the M7C3 to M23C6 transformation during the heat treatments, enhancing the interdendritic mode of fracture both in the as cast and in the annealed condition. (EN)
Materials Science, Multidisciplinary (EN)
Metallurgy & Metallurgical Engineering (EN)
EMBRITTLEMENT (EN)
CREEP (EN)
IMPACT PROPERTIES (EN)
GRAIN-BOUNDARY CARBIDES (EN)
MATERIALS SCIENCE AND TECHNOLOGY (EN)
Αγγλική γλώσσα
INST MATERIALS (EN)
National Technical University of Athens
Digital Library of National Technical University of Athens | Dspace@NTUA
Κεντρική Βιβλιοθήκη Ε.Μ.Π.
Ιδρυματικό Αποθετήριο
Δημοσιεύσεις μελών Δ.Ε.Π. σε περιοδικά



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.