ALUMINUM SPECIMENS OF THE 5052 ALLOY OF 3X5 CM2 DIMENSIONS, ANODIZED [15% H2SO4, C.D.: 6,5 A/DM2, T: 25 C, FOR 7 MIN (15 MM) AND FOR 45 MIN (40 MM)] WITHOUT AND WITH SEALING (H2O, 99 C, FOR 1,5 TO 30 MIN), WERE EXPOSED TO VERY DILUTED ACIDS OF DIFFERENT CONCENTRATIONS (H2SO4, HNO3 AND A MIXTURE OF 50% H2SO4 AND 50%HNO3 OF THE SAME INITIAL CONCENTRATIONS) AND TO AN ATMOSPHERE OF SO2 (G) IN DIFFERENT CONCENTRATIONS OF SO2 WITH A WATER VAPOR SATURATED ATMOSPHERIC CONDITIONS. BASED ON THESE RESULTS A MODEL IS PROPOSED WHERE A PREDICTION IS ATTEMPTED BASED ON THE WEIGHT LOSS OF THE OXIDES AND OF THE HYDRATES OF ALUMINUM IN CONDITIONS OF ACID RAIN. THE BEST BEHAVIOUR FOR ALL CASES STUDIED, WAS THE ONE SHOWNBY THE HYDRATE OF Γ1-AL2O3 FULLY SEALED.
ΔΟΚΙΜΙΑ ΑΛΟΥΜΙΝΙΟΥ ΑΠΟ ΤΟ ΚΡΑΜΑ AL-5052, ΔΙΑΣΤΑΣΕΩΝ 3Χ5 CM2 ΟΞΕΙΔΩΜΕΝΑ (15% H2S04, 6,5 A/DM2, 25 C, 7 MIN-15MM ΚΑΙ 45 ΜΙΝ - 40ΜΜ) ΧΩΡΙΣ 'Η ΜΕ ΣΦΡΑΓΙΣΜΑ (H2O, 99 C, 1,5 'Η 30 MIN), ΕΚΤΕΘΗΚΑΝ ΣΕ ΑΡΑΙΑ ΔΙΑΛΥΜΑΤΑ ΟΞΕΩΝ ΔΙΑΦΟΡΩΝ ΣΥΓΚΕΝΤΡΩΣΕΩΝ(H2SO4, HNO3 ΚΑΙ ΜΙΓΜΑΤΟΣ 50% H2SO4 + 50% ΗΝΟ3 ΤΩΝ ΙΔΙΩΝ ΑΡΧΙΚΩΝ ΣΥΓΚΕΝΤΡΩΣΕΩΝ) ΚΑΙ ΣΕ ΤΕΧΝΗΤΗ ΑΤΜΟΣΦΑΙΡΑ ΜΕ SO2 ΣΕ ΔΙΑΦΟΡΕΣ ΠΕΡΙΕΚΤΙΚΟΤΗΤΕΣ ΚΑΙ ΚΟΡΕΣΜΕΝΟΥΣ ΥΔΡΑΤΜΟΥΣ. ΜΕ ΒΑΣΗ ΤΑ ΑΠΟΤΕΛΕΣΜΑΤΑ, ΚΑΤΑΣΤΡΩΘΗΚΕ ΜΟΝΤΕΛΟ, ΜΕ ΒΑΣΗ ΤΟ ΟΠΟΙΟ, ΜΠΟΡΕΙ ΝΑ ΓΙΝΕΙ ΠΡΟΒΛΕΨΗ ΤΗΣ ΑΠΩΛΕΙΑΣ ΒΑΡΟΥΣ ΤΩΝ ΟΞΕΙΔΙΩΝ ΚΑΙ ΤΩΝ ΥΔΡΙΤΩΝ ΤΟΥ ΑΛΟΥΜΙΝΙΟΥ ΣΕ ΣΥΝΘΗΚΕΣ ΟΞΙΝΗΣ ΒΡΟΧΗΣ. ΤΗΝ ΚΑΛΥΤΕΡΗ ΑΝΤΙΔΙΑΒΡΩΤΙΚΗ ΣΥΜΠΕΡΙΦΟΡΑ ΕΙΧΕ,ΣΕ ΟΛΕΣ ΤΙΣ ΠΕΡΙΠΤΩΣΕΙΣ, Ο ΥΔΡΙΤΗΣ ΤΟΥ Γ1-AL2O3 ΜΕ ΠΛΗΡΗ ΣΦΡΑΓΙΣΗ.
National Documentation Centre (EKT)