A Rietveld analysis of the transformation of (La-Sr-V-O)(reduced) to (La-Sr-V-O)(oxidized) solids and the effect on their surface catalytic properties

 
Το τεκμήριο παρέχεται από τον φορέα :

Αποθετήριο :
Ιδρυματικό Αποθετήριο Ολυμπιάς
δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*
κοινοποιήστε το τεκμήριο



Σημασιολογικός εμπλουτισμός από το EKT
1998 (EL)
A Rietveld analysis of the transformation of (La-Sr-V-O)(reduced) to (La-Sr-V-O)(oxidized) solids and the effect on their surface catalytic properties (EN)
Trikalitis, P. N. (EN)
Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Χημείας (EL)
Trikalitis, P. N. (EN)
The transformation of the crystal phases of the system (La-Sr-V-O)(reduced), having the general formula La1-xSrxVO3 (x=0.0, 0.05, 0.1, 0.2, 0.4, 0.6, 0.8, 0.9, 0.95, 1.0) and the perovskite structure, towards the (La-Sr-V-O)(oxidized) one, was studied using the Rietveld analysis. The oxidized system contains the crystal phases LaVO4, Sr2V2O7 and Sr3V2O8 which originate from the crystal phases LaVO3 and SrVO3 existing in the reduced system. The oxidized solids exhibits surface areas (BET) around 8-10 m(2) g(-1) while the reduced ones much lower similar to 1 m(2) g(-1). SEM studies showed that the oxidized particles exhibits a much more irregular surface with pores, cracks, steps and similar features which lack in the reduced solids. The oxidized solids rich in Sr show also a platelet-like structure. The acid/base function of the surface was studied using the isopropanol decomposition as a test reaction towards propene or acetone. The oxidized forms of the solids exhibits stronger acidic properties as compared to the reduced one and lead to dehydration towards propene while the reduced solids exhibit also considerable dehydrogenation activity. The rest features of catalytic action, like reaction rate and apparent activation energies appear rather similar and a common compensation effect, for the reduced and oxidized solids, is observed. The variation of the reaction path towards dehydrogenation or dehydration is related to the intermediate electronegativity of the solids for both the reduced and the oxidized samples. (C) 1998 Elsevier Science B.V. (EN)
perovskite (EN)
Πανεπιστήμιο Ιωαννίνων
Ιδρυματικό Αποθετήριο Ολυμπιάς
Σχολή Θετικών Επιστημών
Άρθρα σε επιστημονικά περιοδικά ( Ανοικτά)
ΑΠΟΘΕΤΗΡΙΟ "ΟΛΥΜΠΙΑΣ"
Τμήμα Χημείας
Applied Catalysis a-General (EN)
Αγγλική γλώσσα
1998
http://olympias.lib.uoi.gr/jspui/handle/123456789/8033
<Go to ISI>://000072699600014
Elsevier (EN)



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.