Raman scattering in sputtered amorphous Ge25Se75-xBix films (EN)

Mytilineou, E (EN)
Chao, BS (EN)
Papadimitriou, D (EN)

N/A (EN)

Raman spectra of sputtered amorphous Ge25Se75-xBix films, with x from 0 to 19, have been studied. For x = 0 the typical spectrum of an amorphous GeSe3 glass is obtained. It is dominated by the peaks at 200 and 220 cm(-1), characteristic of the Ge(Se-1/2)(4) tetrahedra and a broad peak at 265 cm(-1), due to the excess Se-Se bonds. The intensity of the 200, 220, 265 cm(-1) peaks decrease and a new broad asymmetric peak appears at 175 cm(-1) whose intensity increases with the increase of the amount of Bi incorporated into the films, This later peak is attributed to Bi2Se3 structural units. (EN)

journalArticle

Raman Scattering (EN)
Raman Spectra (EN)
CHALCOGENIDE GLASSES (EN)
Spectrum (EN)

Εθνικό Μετσόβιο Πολυτεχνείο (EL)
National Technical University of Athens (EN)

Journal of Non-Crystalline Solids (EN)

1996


ELSEVIER SCIENCE BV (EN)



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.