PREPARATION AND CHARACTERIZATION OF CERAMIC BEADS WITH HIERARCHICAL POROSITY FABRICATED BY A PHASE INVERSION TEMPLATING METHOD
Vasiliki Chalkia
Elena Marathoniti
Pavlos Pandis
Stella Sklari
Vassilis Stathopoulos
In this study we report the synthesis and characterization of ceramic beads of hierarchical porosity in the meso and macro pore range. The materials preparation is based on the combination of polymer templating and phase inversion methods. Three different kind of ceramic powders: α-alumina (α-Al2O3), yttria stabilized zirconia (YSZ) and apatite type lanthanum silicate oxide (LFSO) were used for the formation of mm monomodal sized beads. High total porosity values were found (40%-75%) depending on the material sintering properties and the preparation method. The pore size distribution revealed graded pores in the range of large meso and macro pore range depending on the thermal treatment of the materials.
(EN)
*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.
PREPARATION AND CHARACTERIZATION OF CERAMIC BEADS WITH HIERARCHICAL POROSITY FABRICATED BY A PHASE INVERSION TEMPLATING METHOD
PREPARATION AND CHARACTERIZATION OF CERAMIC BEADS WITH HIERARCHICAL POROSITY FABRICATED BY A PHASE INVERSION TEMPLATING METHOD
Βοηθείστε μας να κάνουμε καλύτερο το OpenArchives.gr.