DIELECTRIC LOSSES AND IONIC-CONDUCTIVITY OF LIFBA2+
GRAMMATIKAKIS, J
PAPATHANASSIOU, A
BOGRIS, N
MANOLOPOULOS, M
and KATSIKA, V
Ba2+-doped LiF crystals were studied using the “dielectric loss” and
“ionic conductivity” methods. By the first method we have indicated
the existence of two relaxation mechanisms. The first mechanism is
attributed to reorientation of ion-vacancy dipoles by means of
nearest-neighbor to nearest-neighbor jumps. The estimated activation
enthalpy h. and the preexponential factor tau0 are 0.43 eV and 3.30 X
10(-9) sec, respectively. The second mechanism is attributed to
nearest-neighbor to next-nearest-neighbor jumps. The enthalpy parameters
are h(m) = 0.34 eV and tau0 = 2.75 X 10(-8)sec. By the ionic
conductivity method the migration enthalpy of free vacancies is
estimated to be h(m) = 0.67 eV.
(EN)