Carbon covered magnetic nickel nanoparticles embedded in PBT-PTMO polymer: Preparation and magnetic properties

Το τεκμήριο παρέχεται από τον φορέα :
Εθνικό και Καποδιστριακό Πανεπιστήμιο Αθηνών   

Αποθετήριο :
Πέργαμος   

δείτε την πρωτότυπη σελίδα τεκμηρίου
στον ιστότοπο του αποθετηρίου του φορέα για περισσότερες πληροφορίες και για να δείτε όλα τα ψηφιακά αρχεία του τεκμηρίου*



Carbon covered magnetic nickel nanoparticles embedded in PBT-PTMO polymer: Preparation and magnetic properties
Guskos, N. Maryniak, M. Typek, J. Podsiadly, P. Narkiewicz, U. Senderek, E. Roslaniec, Z.
scientific_publication_article
Επιστημονική δημοσίευση - Άρθρο Περιοδικού (EL)
Scientific publication - Journal Article (EN)
2009
Fine particles of a face-centered-cubic phase of Ni covered with a graphite layer were prepared and embedded in a PBT-block-PTMO polymer at a concentration of 0.1 wt%. The mean crystalline size of Ni varied from 8 to 30 nm. A magnetic resonance study of the obtained nanocomposites was carried out in the 4-300 K temperature range using an electron paramagnetic resonance spectrometer. An almost symmetrical and very intense magnetic resonance line was recorded for all the investigated samples. The resonance line was centered at g = 2.253(2) (the resonance field Hr = 3003(1) Gs) and had a peak-to-peak linewidth ΔHpp = 693(2) Gs at room temperature. The amplitude of the resonance line increased with a temperature increase in the low temperature range (T < 40 K) and in the high temperature range (T > 100 K) but was constant at intermediate temperatures. The resonance field Hr decreased and linewidth ΔHpp increased as the temperature decreased from room temperature what was similar to the changes observed for other systems of nanoparticles. The thermal gradient of the resonance field, ΔHr/ΔT, strongly depended on the temperature range. The temperature shift of the resonance field and the linewidth were analyzed in terms of the demagnetizing fields of nonspherical agglomerates. A strong change of linewidth and resonance field was registered below 40 K due to the freezing of the spin system's dynamical magnetic fluctuations. A comparison was made of the results obtained on the Ni/C with the previous measurements on γ-Fe2O3 nanoparticles embedded in a copolymer. © 2009 Elsevier B.V. All rights reserved. (EN)
Αγγλική γλώσσα
Ερευνητικό υλικό ΕΚΠΑ
https://creativecommons.org/licenses/by-nc/4.0/
Εθνικό και Καποδιστριακό Πανεπιστήμιο Αθηνών
Πέργαμος
Άρθρο Περιοδικού (Journal Article)



*Η εύρυθμη και αδιάλειπτη λειτουργία των διαδικτυακών διευθύνσεων των συλλογών (ψηφιακό αρχείο, καρτέλα τεκμηρίου στο αποθετήριο) είναι αποκλειστική ευθύνη των αντίστοιχων Φορέων περιεχομένου.