Surface characterization of monolithic zirconia submitted to different
surface treatments applying optical interferometry and raman
spectrometry
Tzanakakis, Emmanouil
Kontonasaki, Eleana
Voyiatzis, George and
Andrikopoulos, Konstantinos
Tzoutzas, Loannis
This study evaluated roughness parameters and phase transformation of
monolithic zirconia ceramics after various mechanical and laser thermal
treatments. Fully sintered monolithic zirconia cylinder specimens were
divided to five groups, according to the applied surface treatment: CL:
control, GB: grit-blasted with glass particles. AL50: grit-blasted with
50 mu m alumina particles, AL90: grit-blasted with 90 mu m dyed-alumina
particles and FEML: subjected to femto laser thermal treatment. Six
roughness parameters (Sa, Sq, Sz, Sci, Svi and Sdr) were measured by
optical profilometry. Phase transformation in zirconia was determined by
micro-Raman spectroscopy. The highest roughness values were recorded in
AL90 and FEML groups, followed by AL50. AL90 presented statistically
higher monoclinic phase content compared to all other groups. Control
and GB groups presented similar roughness without phase transformation.
Laser thermal treatment causes minimal destruction of the zirconia
surface, and can be suggested as an alternative to other roughening
treratments, for enhancing the adhesive potential to dentin.