Surface characterization of monolithic zirconia submitted to different surface treatments applying optical interferometry and raman spectrometry

This item is provided by the institution :
/aggregator-openarchives/portal/institutions/uoa   

Repository :
Pergamos Digital Library   

see the original item page
in the repository's web site and access all digital files if the item*



Surface characterization of monolithic zirconia submitted to different surface treatments applying optical interferometry and raman spectrometry
Tzanakakis, Emmanouil Kontonasaki, Eleana Voyiatzis, George and Andrikopoulos, Konstantinos Tzoutzas, Loannis
scientific_publication_article
Επιστημονική δημοσίευση - Άρθρο Περιοδικού (EL)
Scientific publication - Journal Article (EN)
2020
This study evaluated roughness parameters and phase transformation of monolithic zirconia ceramics after various mechanical and laser thermal treatments. Fully sintered monolithic zirconia cylinder specimens were divided to five groups, according to the applied surface treatment: CL: control, GB: grit-blasted with glass particles. AL50: grit-blasted with 50 mu m alumina particles, AL90: grit-blasted with 90 mu m dyed-alumina particles and FEML: subjected to femto laser thermal treatment. Six roughness parameters (Sa, Sq, Sz, Sci, Svi and Sdr) were measured by optical profilometry. Phase transformation in zirconia was determined by micro-Raman spectroscopy. The highest roughness values were recorded in AL90 and FEML groups, followed by AL50. AL90 presented statistically higher monoclinic phase content compared to all other groups. Control and GB groups presented similar roughness without phase transformation. Laser thermal treatment causes minimal destruction of the zirconia surface, and can be suggested as an alternative to other roughening treratments, for enhancing the adhesive potential to dentin. (EN)
English
Ερευνητικό υλικό ΕΚΠΑ
https://creativecommons.org/licenses/by-nc/4.0/
University of Athens
Pergamos Digital Library
Journal Article



*Institutions are responsible for keeping their URLs functional (digital file, item page in repository site)